FLEXURAL BEHAVIOR OF FLY ASH-BASED GEOPOLYMER R/C BEAM WITH BAUXITE MATERIAL AS COARSE AGGREGATES

Lisantono, Ade and Sudjati, Johanes Januar and Lianasari, Angelina Eva (2019) FLEXURAL BEHAVIOR OF FLY ASH-BASED GEOPOLYMER R/C BEAM WITH BAUXITE MATERIAL AS COARSE AGGREGATES. International Journal of GEOMATE, 18 (65). pp. 80-85. ISSN 2186-2982

Preview

Text 1T-Geomate-gb.pdf Download (1MB) | Preview

Abstract

Bauxite materials are provided in Indonesia especially in Batam Island. Based on the previous research, this material can be used as coarse aggregates in fly ash-based geopolymer concrete. To study the behavior of fly ash-based geopolymer reinforced concrete beam subjected to bending, this research is conducted. Two fly ash-based geopolymer reinforced concrete beams were made and tested. The first beam was made from normal concrete as a reference beam, while the second beam was fly ash-based geopolymer concrete which was using bauxite as coarse aggregates. Both beams had the same size of 120 mm width and 240 mm in height. Two longitudinal reinforcements with a diameter of 16 mm as tensile reinforcements and a diameter of 13 mm as compressive reinforcements. The stirrups using diameter 6 mm with spacing 100 mm along the span of the beam. Two loading points were applied to the beam using monotonic loading. The beam is a simple beam. The load-carrying capacity of the normal beam and fly ash-based geopolymer concrete beam were compared. Section analysis was also conducted to check the experimental program with the theory. The result shows that the flexural behavior of both beams was similar. Both beams show as ductile beams. The maximum load of the normal concrete beam was 63.00 kN. While the maximum load of the fly ash-based geopolymer concrete was 66.15 kN. The section analysis of both beams closed to the experimental result indicated that the theory can be applied to the fly ash-based geopolymer concrete with bauxite material as coarse aggregates

Actions (login required)

View Item